Alkyd Silicon Paint

  • Catalog Download

  • Recommended Use

    Alkyd silicon paint is a ‘one component’ paint which is heat resistant up to 250°C. It can be used as a single layer or as a top coat on ethyl silicate coating or other heat resistant and compatible coating. This product is recommended for exterior of steel structure expose to high temperature in power plant or refineries, and etc
  • Surface Preparation

    •The surface should be free from any rust, moisture, mill scale, oil and grease. • If the surface is smooth, it should rub by sand paper. • Mechanical and chemical surface preparation methods should be performed depending on the type of contamination, the coating system, environmental condition and service life. • The damaged area of primer and subsequent layer should repair.   • Apply the paint immediately followed by surface preparation.
  • Application Procedure

    • Flush equipment with cleaner before use • Stir two components with a power mixer. Notice pot life time and mixing ratio • Use Shakiba`s thinner for adjusting the viscosity • The thinner should be added gradually • The consumption depends on temperature and type of equipment and thickness paint • Clean all equipment with Shakiba`s thinner
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Density , solid contents theoretical coverage are dependent on color - Pot life, drying time is dependent on air and steel temperature, applied film thickness. - Never apply coatings under environmental condition. - Adjusting the viscosity & pressure. For better adhesion on un steel, we offer wash primer as on under. - This information given 25°C temperature and changed temperature cause to change data. - Don’t use different thinner; otherwise we decline all responsibilities of it. - For more information, please call to sale engineering expert.

Heat Resistant Silicon Coatings

  • Catalog Download

  • Recommended Use

    Pure silicone is a one component coating. It can be applied per one coat or as a topcoat on recommended primers such as ethyl silicate. This product is suitable for metallic substrates exposed to high temperatures such as stoves. Chemical factories, petrochemical sites, refineries and power plants. This paint is pure silicon which is heat resistant up to 600 0c
  • Surface Preparation

    - The surface should be free form any rust, moisture, mill scale, oil & grease - Mechanical & chemical surface preparation methods should be performed depending on the type of contamination, the coating system environ mental condition & the service life - Apply the paint immediately followed by surface preparation
  • Application Procedure

    • Flush equipment withrecommended cleaner before use . • Stir paint with a power mixer(max.2min) . • Use Shakiba`s thinner for adjusting the viscosity . • The thinner should be added gradually . • The consumption depends on temperature and type of equipment and thickness paint • Clean all equipment with Shakiba`s thinner
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Drying time is dependent or air and steel temperature, applied film thickness. - Never apply coatings under environmental condition. - Adjusting the viscosity & pressure. - This information given 25°C temperature and changed temperature cause to change data. - Don’t use different thinner and recommended to avoid high thickness of the paint r; otherwise we decline all responsibilities of it. - For more information, please call to sale engineering expert.

Heat Resistant Acrylic Silicon Coatings

  • Catalog Download

  • Recommended Use

    Acrylic silicone is a one component coating. This paint is a silicone- modified acrylic which is heat resistant up to 250`c. The product is recommended for exteriors of steel structures. Exposed to high temperatures in power plant, oil production and refining plants.
  • Surface Preparation

    -The surface should be free form any rust, moisture, mill scale, oil & grease - Mechanical & chemical surface preparation methods should be performed depending on the type of contamination, the coating system environ mental condition & the service life - Apply the paint immediately followed by surface preparation
  • Application Procedure

    • Flush equipment with recommended cleaner before use • Stir paint with a power mixer (max.2.min). • Use Shakiba`s thinner for adjusting the viscosity • The thinner should be added gradually • The consumption depends on temperature and type of equipment and thickness paint • Clean all equipment with Shakiba`s thinner .
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Drying time is dependent or air and steel temperature, applied film thickness. - Never apply coatings under environmental condition. - Adjusting the viscosity & pressure. - This information given 25°C temperature and changed temperature cause to change data. - Don’t use different thinner and recommended to avoid high thickness of the paint; otherwise we decline all responsibilities of it. - For more information, please call to sale engineering expert.

Inorganic Ethyl Silicate Zinc Rich Primer (I.Z.P)

  • Catalog Download

  • Recommended Use

    I.Z.P is a two component coating. The high load of zinc dust prevents the corrosion through a galvanic protection the product can with stand the temperature up to 400°C .This primer is not recommended for spillage of acid or alkaline solution. Other characteristics of this product are resistance against UV expose. This paint has high resistance to corrosion moisture, chemical environments, petrol materials Food, industrial oils, pipe, tank, hull & deck of ships, reactor etc.
  • Surface Preparation

    -The surface should be free form any rust, moisture, mill scale, oil & grease - Mechanical & chemical surface preparation methods should be performed depending on the type of contamination, the coating system environ mental condition & the service life - For ferrous & Steel use blast in accordance with sa2 or sa2 ½ & remove all the abrasive residues & dust from the surface after sandblasting. - Apply the paint immediately followed by surface preparation .
  • Application Procedure

    - Flush equipment with recommended cleaner before use - Add solution to base in the proper Mixing continue stirring for 5-10 Minutes. - Stir during application to keep the material homogenized - Check thickness of dry coating non-destructive thickness gauge - Prevent contact with water until The freshly applied coating is at least dry to touch - Zinc powder can be absorbed water and humidity and may be cause to create the fire, be careful of this situation and be care the discharge of ecstatic electricity.
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Pot life, drying time is dependent on air, steel temperature, applied film thickness and humidity. - Never apply coatings under environmental condition. - Adjusting the viscosity & pressure   - Recoating time dependent temperature and humidity. - This information given 25°C  temperature and changed temperature cause to change data. - Don’t use different thinner; otherwise we decline all responsibilities of it. - For more information, please call to sale engineering expert. - Over 100(μ) thickness may cause create the cracks.