Epoxy High Build Top Coat

  • Catalog Download

  • Recommended Use

    Epoxy topcoat is a two component coating. It provides a glossy, level and smooth film which is resistance against scratching & abrasion as well as humidity and chemicals suitable as finish coat in various epoxy paint systems and excellent chemical resistance against weak acid and alkalis. This product is also recommended for drinking water tanks and pipes. Such a coating system is recommended for power plants, petrochemical & oil refining, machinery, steel structures and etc.
  • Surface Preparation

    - The surface should be free form any rust, moisture, mill scale, oil & grease - Mechanical & chemical surface preparation methods should be performed depending on the type of contamination, the coating system environ mental condition & the service life - Apply the paint immediately followed by surface preparation
  • Application Procedure

    - Flush equipment with recommended cleaner before use - Stir component A (base) with a Power Mixer. - Add hardener to base in the proper Mixing continue stirring for 5-10 Minutes. - After 20 – 30 minutes add Shakiba’s thinner for ready to use - Use Shakiba’s thinner for adjusting the viscosity. - The consumption depends on temperature & type of equipment & thickness pai
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Density , solid contents theoretical coverage are dependent on color - Pot life, drying time is dependent on air and steel temperature, applied film thickness. - Never apply coatings under environmental condition. -Adjusting the viscosity & pressure. -This information given 25 °C temperature and changed temperature cause to change data. -Don’t use different thinner; otherwise we decline all responsibilities of it. -For more information, please call to sale engineering expert.

Epoxy Putty

  • Catalog Download

  • Recommended Use

    It is a two component putty base on epoxy resin. It is generally used to fill porosity and narrow cracks and achieve to uniform surface. It can be applied on different kind surfaces such as cement, plaster, and etc.
  • Surface Preparation

    • The surface should be free from any rust, moisture, mill scale, oil and grease • Mechanical and chemical surface preparation methods should be performed depending on the type of contamination, the coating system environmental condition and service life. • Apply the putty immediately followed by surface preparation.
  • Application Procedure

    • Flush equipment with cleaner before use • Stir two components with a power mixer. Notice pot life time and mixing ratio • Use Shakiba`s thinner for adjusting the viscosity • The thinner should be added gradually • The consumption depends on temperature and type of equipment and thickness paint • Clean all equipment with Shakiba`s thinner
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Density , solid contents theoretical coverage are dependent on color - Pot life, drying time is dependent on air and steel temperature, applied film thickness. - Never apply coatings under environmental condition. -Adjusting the viscosity & pressure. For better adhesion on un steel, we offer wash primer as on under. -This information given 25°C temperature and changed temperature cause to change data. -Don’t use different thinner; otherwise we decline all responsibilities of it.

Glass Flake Epoxy Polyamine Primer

  • Catalog Download

  • Recommended Use

    Glass flake is a two component epoxy coating with general properties of epoxy polyamine resin and extra characteristic includes excellent mechanical strength and high chemical resistance against weak acids, alkalis, and high performance coating for new and old steel is out standing properties. It protects both steel and concrete structures including marine structures, tank’s oil, petroleum and heavy industrial facilities and suitable sea water immersion
  • Surface Preparation

    • The surface should be free from any rust, moisture, mill scale, oil and grease • Mechanical and chemical surface preparation methods should be performed depending on the type of contamination, the coating system environmental condition and service life. • Apply the paint immediately followed by surface preparation.
  • Application Procedure

    • Flush equipment with cleaner before use • Stir two components with a power mixer. Notice pot life time and mixing ratio • Use Shakiba`s thinner for adjusting the viscosity • The thinner should be added gradually • The consumption depends on temperature and type of equipment and thickness paint • Clean all equipment with Shakiba`s thinner .
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Density , solid contents theoretical coverage are dependent on color - Pot life, drying time is dependent on air and steel temperature, applied film thickness. - Never apply coatings under environmental condition. -Adjusting the viscosity & pressure. For better adhesion on un steel, we offer wash primer as on under. -This information given 25°C temperature and changed temperature cause to change data. -Don’t use different thinner; otherwise we decline all responsibilities of it. -For more information, please call to sale engineering expert

Iron Oxide Epoxy Polyamine Primer

  • Catalog Download

  • Recommended Use

    It is a two component coating base on epoxy resin and as a general purpose rust preventing primer for epoxy system on steel and other metal surfaces, and high chemical resistance. It has very good adhesion to and used for steel structure, machineries, pipes, tanks, bridges, power plants, refineries and industrial environments..
  • Surface Preparation

    • The surface should be free from any rust, moisture, mill scale, oil and grease • Mechanical and chemical surface preparation methods should be performed depending on the type of contamination, the coating system environmental condition and service life.
  • Application Procedure

    • Flush equipment with cleaner before use • Stir two components with a power mixer. Notice pot life time and mixing ratio • Use Shakiba`s thinner for adjusting the viscosity • The thinner should be added gradually • The consumption depends on temperature and type of equipment and thickness paint • Clean all equipment with Shakiba`s thinner .
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Density , solid contents theoretical coverage are dependent on color - Pot life, drying time is dependent on air and steel temperature, applied film thickness. - Never apply coatings under environmental condition. -Adjusting the viscosity & pressure. For better adhesion on un steel, we offer wash primer as on under. -This information given 25°C temperature and changed temperature cause to change data. -Don’t use different thinner; otherwise we decline all responsibilities of it. -For more information, please call to sale engineering expert.

Anti-acid Epoxy Paint

  • Catalog Download

  • Recommended Use

    Anti- acid epoxy is a two component coating. This paint formulated for concrete to provide resistance against Spillage of various chemicals such as alkaline, acids and salt solutions. This product can be used as a protective coating in factories warehouses Silos, etc. It provides long term resistance to corrosion even under mechanical strength condition.
  • Surface Preparation

    -The surface should be free form any rust, moisture, mill scale, oil & grease - Mechanical & chemical surface preparation methods should be performed depending on the type of contamination, the coating system environ mental condition & the service life - Apply the paint immediately followed by surface preparation
  • Application Procedure

    • Flush equipment with recommended cleaner before use . • Stir component A (base) with a Power Mixer. • Add hardener to base in the proper Mixing continue stirring for 5 minutes. • Since the pot life is limited & shortened by high temperatures, do not mix more material than will be used in 1 hours at 25°C
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Density , solid contents theoretical coverage are dependent on color - Pot life, drying time is dependent on air and steel temperature, applied film thickness. - Never apply coatings under environmental condition. -This information given 25°C temperature and changed temperature cause to change data. - For more information, please call to sale engineering expert.

Epoxy Polyamine Top Coat

  • Catalog Download

  • Recommended Use

    Epoxy polyamine topcoat is a two component coating. this product has good resistance to splash and fumes of an acids, alkalis, solvent and fresh and salt water steel and off shore structures, as well as exterior tank and pipe surfaces can be coated by this paint to obtain higher resistance in corrosive environment. Such as coating system is recommended for power plants, petrochemical & oil refining and machinery.
  • Surface Preparation

    -The surface should be free form any rust, moisture, mill scale, oil & grease - Mechanical & chemical surface preparation methods should be performed depending on the type of contamination, the coating system environ mental condition & the service life - Apply the paint immediately followed by surface preparation .
  • Application Procedure

    - Flush equipment with recommended cleaner before use - Stir component A (base) with a Power Mixer. - Add hardener to base in the proper Mixing continue stirring for 5-10 Minutes. - After 20 – 30 minutes add Shakiba’s thinner for ready to use - Use Shakiba’s thinner for adjusting the viscosity. -The consumption depends on temperature & type of equipment & thickness paint
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Density , solid contents theoretical coverage are dependent on color - Pot life, drying time is dependent on air and steel temperature, applied film thickness. - Never apply coatings under environmental condition. -Adjusting the viscosity & pressure. -This information given 25°C temperature and changed temperature cause to change data. -Don’t use different thinner; otherwise we decline all responsibilities of it. -For more information, please call to sale engineering expert.

Zinc Chromate- Iron Oxide Epoxy Polyamine Primer

  • Catalog Download

  • Recommended Use

    It is a two component coating base on epoxy resin and includes zinc chromate as anti-corrosive pigment so this is one of the best anti-corrosive products which are recommended in the severe atmosphere or chemical condition. It has very good adhesion to and used for steel structure, machineries, pipes, tanks, bridges, power plants, refineries and industrial environments.
  • Surface Preparation

    •The surface should be free from any rust, moisture, mill scale, oil and grease • Mechanical and chemical surface preparation methods should be performed depending on the type of contamination, the coating system environmental condition and service life. • Apply the paint immediately followed by surface preparation.
  • Application Procedure

    • Flush equipment with cleaner before use • Stir two components with a power mixer. Notice pot life time and mixing ratio • Use Shakiba`s thinner for adjusting the viscosity • The thinner should be added gradually • The consumption depends on temperature and type of equipment and thickness paint
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Density , solid contents theoretical coverage are dependent on color - Pot life, drying time is dependent on air and steel temperature, applied film thickness. - Never apply coatings under environmental condition. -Adjusting the viscosity & pressure. For better adhesion on un steel, we offer wash primer as on under. -This information given 25°C temperature and changed temperature cause to change data. -Don’t use different thinner; otherwise we decline all responsibilities of it. -For more information, please call to sale engineering expert .

Zinc Phosphate Epoxy Polyamine Primer

  • Catalog Download

  • Recommended Use

    It is a two component coating base on epoxy resin and includes zinc phosphate as anti-corrosive pigment so this is one of the best anti-corrosive products which are recommended in the severe atmosphere or chemical condition. This primer can be coated by a variety of compatible mid or top coats such as epoxy, polyurethane, and etc. It has very good adhesion and used for steel structure, machineries, pipes, tanks, bridges, power plants, refineries and industrial environments.
  • Surface Preparation

    •The surface should be free from any rust, moisture, mill scale, oil and grease • Mechanical and chemical surface preparation methods should be performed depending on the type of contamination, the coating system environmental condition and service life. • Apply the paint immediately followed by surface preparation .
  • Application Procedure

    • Flush equipment with cleaner before use • Stir two components with a power mixer. Notice pot life time and mixing ratio • Use Shakiba`s thinner for adjusting the viscosity • The thinner should be added gradually • The consumption depends on temperature and type of equipment and thickness paint • Clean all equipment with Shakiba`s thinner .
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Density , solid contents theoretical coverage are dependent on color - Pot life, drying time is dependent on air and steel temperature, applied film thickness. - Never apply coatings under environmental condition. -Adjusting the viscosity & pressure. For better adhesion on un steel, we offer wash primer as on under. -This information given 25°C temperature and changed temperature cause to change data. -Don’t use different thinner; otherwise we decline all responsibilities of it. -For more information, please call to sale engineering expert.

Solvent Free Epoxy

  • Catalog Download

  • Recommended Use

    Epoxy polyamine solvent free is two component coating. This product provides long term resistance to corrosion even under aggressive conditions. Other characteristics of this paint are high chemical resistance acids and alkalis. Applicable in high film thickness. As a solvent free epoxy coating with excellent chemical and mechanical properties. Suitable for coating Industrial environments and both marine. Concrete in high wear services as well as dry abrasive blasted
  • Surface Preparation

    -The surface should be free form any rust, moisture, mill scale, oil & grease - Mechanical & chemical surface preparation methods should be performed depending on the type of contamination, the coating system environ mental condition & the service life - Apply the paint immediately followed by surface preparation .
  • Application Procedure

    - Flush equipment with recommended cleaner before use - Stir component A (base) with a Power Mixer. - Add hardener to base in the proper Mixing continue stirring for 5 minutes. - Since the pot life is limited & shortened by high temperatures, do not mix more material than will be used in the pot life period
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Density , solid contents theoretical coverage are dependent on color - Pot life, drying time is dependent on air and steel temperature, applied film thickness. - Never apply coatings under environmental condition. -This information given 25°C temperature and changed temperature cause to change data. -For more information, please call to sale engineering expert.

Zinc Chromate Epoxy Polyamine Primer

  • Catalog Download

  • Recommended Use

    It is a two component coating base on epoxy resin and includes zinc chromate as anti-corrosive pigment so this is one of the best anti-corrosive products which are recommended in the severe atmosphere or chemical condition. This primer can be coated by a variety of compatible mid or top coats such as epoxy, polyurethane, and etc. It has very good adhesion to and used for steel structure, machineries, pipes, tanks, bridges, power plants, refineries and industrial environments.
  • Surface Preparation

    •The surface should be free from any rust, moisture, mill scale, oil and grease • Mechanical and chemical surface preparation methods should be performed depending on the type of contamination, the coating system environmental condition and service life. • Apply the paint immediately followed by surface preparation
  • Application Procedure

    • Flush equipment with cleaner before use • Stir two components with a power mixer. Notice pot life time and mixing ratio • Use Shakiba`s thinner for adjusting the viscosity • The thinner should be added gradually • The consumption depends on temperature and type of equipment and thickness paint • Clean all equipment with Shakiba`s thinner .
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Density , solid contents theoretical coverage are dependent on color - Pot life, drying time is dependent on air and steel temperature, applied film thickness. - Never apply coatings under environmental condition. -Adjusting the viscosity & pressure. For better adhesion on un steel, we offer wash primer as on under. -This information given 25°C temperature and changed temperature cause to change data. -Don’t use different thinner; otherwise we decline all responsibilities of it. -For more information, please call to sale engineering expert.

Zinc Phosphate-Iron Oxide Epoxy Polyamine Primer

  • Catalog Download

  • Recommended Use

    It is a two component coating base on epoxy resin and includes zinc phosphate as anti-corrosive pigment so this is one of the best anti-corrosive products which are recommended in the severe atmosphere or chemical condition. It has very good adhesion to and used for steel structure, machineries, pipes, tanks, bridges, power plants, refineries and industrial environments.
  • Surface Preparation

    •The surface should be free from any rust, moisture, mill scale, oil and grease • Mechanical and chemical surface preparation methods should be performed depending on the type of contamination, the coating system environmental condition and service life. • Apply the paint immediately followed by surface preparation .
  • Application Procedure

    • Flush equipment with cleaner before use • Stir paint with a power mixer • Use Shakiba`s thinner for adjusting the viscosity • The thinner should be added gradually • The consumption depends on temperature and type of equipment and thichness paint • Clean all equipment with Shakiba`s thinner .
  • Safety

    - This product is flammable it must be kept away from heat, flash & flame - keep container closed use with adequate ventilation & Earth - Prolonged & repeated contact with skin may be harmful - In case of eye contact flush with plenty of water and check with a medical doctor.
  • Note

      - Density , solid contents theoretical coverage are dependent on color - Pot life, drying time is dependent on air and steel temperature, applied film thickness. - Never apply coatings under environtmental condition. -Adjusting the viscosity & pressure. For better adhesion on unsteel, we offer wash primer as on under. -This information given 25°C temperatures and changed temperature cause to change data. -Don’t use different thinner; otherwise we decline all responsibilities of it. -For more information, please call to sale engineering expert.